| BORE DIAMETER | 0.9995 INCHES MINIMUM AND 1.0000 INCHES MAXIMUM |
| HARDNESS RATING | UNABLE TO DECODE |
| HARDNESS RATING | |
| INNER MEMBER WIDTH | 1.373 INCHES MINIMUM AND 1.375 INCHES MAXIMUM |
| LUBRICATION FEATURE | UNABLE TO DECODE |
| MATERIAL DOCUMENT AND CLASSIFICATION | AMS5629 H1000 INTERNATIONAL STD/SPEC ALL MATERIAL RESPONSES INNER MEMBER |
| MATERIAL DOCUMENT AND CLASSIFICATION | AMS5643 INTERNATIONAL STD/SPEC ALL MATERIAL RESPONSES OUTER RACE MEMBER |
| MATERIAL | PLASTIC POLYTETRAFLUOROETHYLENE RACE LINER |
| MATERIAL | STEEL CORROSION RESISTING INNER MEMBER |
| MATERIAL | STEEL CORROSION RESISTING OUTER RACE MEMBER |
| OUTER MEMBER WIDTH | 1.000 INCHES MINIMUM AND 1.010 INCHES MAXIMUM |
| OUTER MEMBER OUTSIDE DIAMETER | 2.1245 INCHES MINIMUM AND 2.1250 INCHES MAXIMUM |
| PART NAME ASSIGNED BY CONTROLLING AGENCY | BEARING, PLAIN, SELF-LUBRICATING, SELF-ALIGNING, LOW SPEED, WIDE, GROOVED RACE, -65 TO +325 F |
| SPECIAL FEATURES | LETTER C INDICATES PH13-8 BALL MATERIAL. LETTER A INDICATES TESTED TO 100,000 CYCLES. P = ZINC-NICKEL OR CADMIUM PLATING. MATERIAL - BALL: PH13-8 CRES PER AMS5629 H1000. RACE: 17-4PH CRES PER AMS5643. LINER: PTFE SHALL BE INCLUDED IN THE LINER. HARNESS RATING IS BEFORE SWAGING. FINISH - RACE: PLATING, WHEN SPECIFIED, SHALL BE ZINC-NICKEL PLATING PER AMS2417, TYPE 2, GRADE B OR CADMIUM PLATING PER AMS-QQ-P-416, TYPE II, CLASS 2. PLATING SHALL BE ON THE OUTSIDE DIAMETER SURFACE AND ON THE FLATS BETWEEN THE OUTSIDE DIAMETER AND THE V-GROOVES. THE PLATING RUNOUT SHALL OCCUR EITHER IN THE V-GROOVES OR ON THE SIDE FACE REAS BETWEEN THE V-GROOVES AND THE BALL. BALL: PASSIVATE PER AMS2700, METHOD 1 (NITRIC ACID) OR METHOD 2 (CITRIC ACID), OR ASTM A967. CITRIC 1, CITRIC 2, AND CITRIC 3 ARE ACCEPTABLE. (AMS2700, METHOD 1, TYPE 8 IS PROHIBITED ON BEARINGS MANUFACTURED WITH 440C AFTER JUNE 1, 2018). |
| STATIC RADIAL LOAD RATING | 104000 POUNDS |
| STYLE DESIGNATOR | WITH INSERT AND/OR LINER WITH STAKING GROOVE |
| SURFACE TREATMENT DOCUMENT AND CLASSIFICATION | |
| SURFACE TREATMENT | |
| SURFACE TREATMENT | UNABLE TO DECODE |